Barril e parafuso de extrusora bimetálicos Arburg
Informações técnicas detalhadas
| Base Material |
1)38CrMoAlA(JIS SACM645)
2)Cr12MOV(JIS SKD-11)
3)4Cr5MoSiV1(JIS SKD-61) 4)42CrMo(AISI 4140)
5)9Cr18MoV
|
| Bimetallic Alloy Materials |
1)Fe-based alloy
2)Ni-based alloy/Deloro alloy
3)Co-based alloy
4)NiCo-based alloy
5)Tungsten carbide/Wolfram carbide
|
| Bimetallic Alloy level |
Level A - containing Tungsten of 40%
Level B - containing tungsten of 25%
Level C - containing tungsten of 9.5%
|
| Designing |
Screw structure and compression
ratio can be designed according
to different products & different
clamping force requirement.
|
| Treatment Technology |
1)Longer time Gas Nitriding treatment
2)special anti-wear & abrasion alloy (bimetallic)
3)tungsten carbide
4)cobalt base alloy
5)stainless steel
6)Gh113 nickel based alloy
Treatment
Nitriding treatment(>100 Hours)
Depth of Nitrided Layer: 0.5-0.8 mm
Hardness of Nitrided Layer: >950Hv
Hard Chrome Plating treatment:
Thickness of Hard Chrome Plating Layer: 0.03-0.08mm
Hardness of Hard Chrome Plating Layer: ≥950HV
Nickel alloy plating.treatment:
Bimetallic Barrel Centrifugal Casting (Inlay Alloy)
Bimetallic Screw: Plasma Alloy Coating Spraying
Depth of Bimetallic Layer: >2mm
Hardness of Bimetallic Layer: HRC55°-65°
|
| Material Application |
1)General Plastics
2)ABS,PA,PC,PE,PET,PP,PS,EVA,PU,PVC,U-PVC,etc
3)PA + GF(Glass Fiber)
4)Flame-resistant Reinforced Plastics
5)Modified Engineering Plastics
6)All kinds of Mixed Recycled Material(in Scrap or Granule),etc
|
| Basic Infomation |
Surface Roughness :Ra0.4um
Linearity of the screw: ≤0.015mm
Linear axis limit: ≤0.02mm
Hardness after Hardening & Tempering: HB260-300
Fragility of Nitration:≤Two grade
|
| General Terms |
Means of transport: Ocean,Air,Express
Production time: About 30 days after we receive the deposit and lead time will different according to the order quantity.
|
| Warranty period |
1-2years(Depends on the plastic raw materials)
Bimetallic: much longer lifetime.
|
| Competitive Edge |
1.Long lifetime,low energy consumption.
2.Wonderful plasticizing
3. Top-quality bimetallic screw and barrel
4. High wear resistance, resistance to corrosion
5. Fast and On time delivery
6. Best customer after-sale service!
|
Método de produção de parafuso bimetálico:
Spray de plasma liga de revestimento de pulverização ou Wc/Co toda solda
Soldagem plasma PTA pó aplica-se os eletrodos positivos e negativos do arco de soldagem, permitindo que o caminho da soldadura para ser completamente, soldadas com o material de base. A mínima possibilidade do caminho da soldadura, tornando-se menos rígida totalmente impede que a camada de soldadura da descascando – efetivamente, atualizando o tempo de vida dos parafusos.
Características proeminentes do parafuso bimetálico e barril:
Dureza HRC55-65 excepcional resistência à corrosão.
Camada de dureza atinge acima de 2mm de espessura. Dureza não diminui com a profundidade.
Dureza não diminui sob a temperatura normal.
Abrsion resistência / resistência ao desgaste na camada endurecida é 2 ~ 3 vezes maior do que o Tratado por tratamento térmico convencional.
Nós especializamo-na fabricação de vários tipos de parafusos, os barris podem ser aplicados em todos os tipos de injeção de moldagem máquina extrusora de alimentação quente de borracha, extrusora de alimentação fria de borracha, pin barril frio alimentar de extrusora, extrusora de plástico com especificações diferentes para haitiano, Demag, Toshiba, Husky, Nissei etc.Podemos fornecer os modelos de parafuso incluindo passo variável e profundidade variável, passo variável e igual profundidade, profundidade variável e passo igual e igual profundidade e pitch.Tipo do sulco multi morre, tipo composto, tipo de mistura e separação tipo.